15620F1 Harris Stay-Silv 15% Silver Solder

15620 F1

15620F1 Harris Stay-Silv 15% Silver Solder

Coburn's Product #: 26400804

Mfg#: 15620F1

Brand: Harris Products

Attributes

  • 🔹: Wide melting range allows operators to fill loose connections and cap or build-up around finished joint
  • 🔹: Flows into tight connections when heated above its liquidus temperature
  • 🔹: Excellent for situations where close fit-up does not exist and where thermal expansion and service vibration are involved
  • 🔹: Flux not required for copper brazing as it is self-fluxing
  • 🔹: Can be used to braze brass or copper-to-brass with the use of appropriate brazing flux
  • 🔹: Suitable for brazing low nickel (10% maximum) copper/nickel base metals
  • 🔹: Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
  • 🔹: Recommended joint clearance of 0.003" - 0.006" (0.08 mm - 0.15 mm)
  • 🔹: Conforms to the EU Reach and RoHS directive
  • Type: Solder
  • Length: 20

    • 🔹: Wide melting range allows operators to fill loose connections and cap or build-up around finished joint
    • 🔹: Flows into tight connections when heated above its liquidus temperature
    • 🔹: Excellent for situations where close fit-up does not exist and where thermal expansion and service vibration are involved
    • 🔹: Flux not required for copper brazing as it is self-fluxing
    • 🔹: Can be used to braze brass or copper-to-brass with the use of appropriate brazing flux
    • 🔹: Suitable for brazing low nickel (10% maximum) copper/nickel base metals
    • 🔹: Not recommended for brazing steel or other ferrous metals due to sufficient lack of joint ductility
    • 🔹: Recommended joint clearance of 0.003" - 0.006" (0.08 mm - 0.15 mm)
    • 🔹: Conforms to the EU Reach and RoHS directive
    • Type: Solder
    • Length: 20